Zytel® 80G43HS1L BK104 is a 43% glass fiber reinforced, heat stabilised, black polyamide 66 resin with superior impact resistance.
General information Value Unit Test Standard
Resin Identification PA66-IGF43 - -
Part Marking Code >PA66-IGF43< - ISO 11469
Rheological properties dry / cond Unit Test Standard
Viscosity number 137 / * cm³/g ISO 307, 1157, 1628
Moulding shrinkage, parallel 0.2 / * % ISO 294-4, 2577
Moulding shrinkage, normal 0.6 / * % ISO 294-4, 2577
Mechanical properties dry / cond Unit Test Standard
Tensile Modulus 11700 / - MPa ISO 527-1/-2
Stress at break 169 / - MPa ISO 527-1/-2
Strain at break 3.3 / - % ISO 527-1/-2
Flexural Modulus 10300 / - MPa ISO 178
Charpy impact strength, 23°C 90 / - kJ/m² ISO 179/1eU
Charpy notched impact strength 　 　 ISO 179/1eA
23°C 23 / - kJ/m² 　
-40°C 15 / - kJ/m² 　
Izod notched impact strength 　 　 ISO 180/1A
23°C 23/- kJ/m² 　
-40°C 14/- kJ/m² 　
Izod impact strength, 23°C 78/- kJ/m² ISO 180/1U
Thermal properties dry/cond Unit Test Standard
Melting temperature, 10°C/min 262/* °C ISO 11357-1/-3
Temp. of deflection under load 　 　 ISO 75-1/-2
1.8 MPa 250/* °C 　
0.45 MPa 261/* °C 　
Vicat softening temperature, 50°C/h, 50N 215/* °C ISO 306
Flammability dry/cond Unit Test Standard
Burning Behav. at 1.5mm nom. thickn. HB/* class IEC 60695-11-10
Thickness tested 1.5/* mm IEC 60695-11-10
Burning Behav. at thickness h HB/* class IEC 60695-11-10
Thickness tested 0.75/* mm IEC 60695-11-10
Oxygen index 27/* % ISO 4589-1/-2
Flammability, 3.0mm HB/* - IEC 60695-11-10
Other properties dry/cond Unit Test Standard
Humidity absorption, 2mm 1.5/* % Sim. to ISO 62
Water absorption, 2mm 4.9/* % Sim. to ISO 62
Density 1430/* kg/m³ ISO 1183