PA66 AKV 30 H2.0 901510德國朗盛Durethan 30%玻纖熱老化穩定尼龍66塑料（18024445500）

PA 66, 30 % glass fibers, injection molding, heat-aging stabilized

ISO/ ASTM

ISO Shortname: ISO 1874-PA 66, GHR, 14-100, GF30

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 290 °C / MT 80 °C; 600 bar % ISO 294-4 0.39　
C Molding shrinkage, transverse 60x60x2; 290 °C / MT 80 °C; 600 bar % ISO 294-4 0.93　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.07　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.13　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 10000 6000
C Nominal strain at break 50 mm/min % ISO 527-1,-2 4.4 6.7
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 175 110
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 6.0
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 75 85
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 60 60
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA < 10 14
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA < 10 < 10
Charpy notched impact strength -40 °C kJ/m² ISO 179-1eA < 10 < 10
Izod impact strength 23 °C kJ/m² ISO 180-1U 60　
Izod impact strength -30 °C kJ/m² ISO 180-1U 55　
Izod notched impact strength -30 °C kJ/m² ISO 180-1A < 10 < 10
Izod notched impact strength -40 °C kJ/m² ISO 180-1A < 10 < 10
Flexural modulus 2 mm/min MPa ISO 178-A 9200 5700
Flexural strength 2 mm/min MPa ISO 178-A 270 180
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.0 6.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 265 150
C Puncture maximum force 23 °C N ISO 6603-2 900 1160
C Puncture maximum force -30 °C N ISO 6603-2 800　
C Puncture energy 23 °C J ISO 6603-2 2.8 5.4
C Puncture energy -30 °C J ISO 6603-2 2.3　
Ball indentation hardness　N/mm² ISO 2039-1 220 120

Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 263　
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 >240　
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 250　
Vicat softening temperature 50 N; 120 °C/h °C ISO 306 > 230　
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.3　
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 0.9　
C Burning behavior UL 94 (1.6 mm) 1.6 mm Class UL 94 HB　
Burning behavior UL 94 3.2 mm Class UL 94 HB　
C Oxygen index Method A % ISO 4589-2 23　
Resistance to heat (ball pressure test)　°C IEC 60695-10-2 253　
Glow wire test (GWFI) 0.8 mm °C IEC 60695-2-12 700　
Glow wire test (GWFI) 1.6 mm °C IEC 60695-2-12 700　
Glow wire test (GWFI) 3.0 mm °C IEC 60695-2-12 700　
Burning behavior US-FMVSS302 >=1.0 mm　ISO 3795 passed　
C Vicat softening temperature 50 N; 50 °C/h °C ISO 306 230　

Electrical properties (23 °C/50 % r. h.)
C Relative permittivity 100 Hz - IEC 60250 4.0 12
C Relative permittivity 1 MHz - IEC 60250 4.0 4.0
C Dissipation factor 100 Hz 10-4 IEC 60250 120 2700
C Dissipation factor 1 MHz 10-4 IEC 60250 190 800
C Volume resistivity　Ohm·m IEC 60093 1E13 1E10
C Surface resistivity　Ohm IEC 60093 1E15 1E13
C Electric strength 1 mm kV/mm IEC 60243-1 35 30
C Comparative tracking index CTI Solution A V IEC 60112 475　

Other properties (23 °C)
C Water absorption (Saturation value) Water at 23 °C % ISO 62 5.5　
C Water absorption (Equilibrium value) 23 °C; 50 % RH % ISO 62 2.0　
C Density　kg/m³ ISO 1183 1360　
Bulk density　kg/m³ ISO 60 700　

Processing conditions for test specimens
C Injection molding-Melt temperature　°C ISO 294 290　
C Injection molding-Mold temperature　°C ISO 294 80　

Processing recommendations
Drying temperature dry air dryer　°C - 80　
Drying time dry air dryer　h - 2-6　
Residual moisture content　% Acc. to Karl Fischer　0.03-0.12　
Melt temperature (Tmin - Tmax)　°C - 280-300　
Mold temperature　°C - 80-120　

C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.