PA66 80G33HS1L BK104美國杜邦Zytel® 33%玻纖增強耐沖擊聚酰胺66尼龍塑料（18024445500）

Zytel® 80G33HS1L BK104 is a 33% glass fiber reinforced heat stabilised polyamide 66 resin with outstanding impact resistance developed
using DuPont Super Tough technology.
General information Value Unit Test Standard
Resin Identification PA66-IGF33 - -
Part Marking Code >PA66-IGF33< - ISO 11469
Rheological properties dry / cond Unit Test Standard
Moulding shrinkage, parallel 0.3 / * % ISO 294-4, 2577
Moulding shrinkage, normal 0.7 / * % ISO 294-4, 2577
Mechanical properties dry / cond Unit Test Standard
Tensile Modulus 8800 / 6500 MPa ISO 527-1/-2
Stress at break 148 / 112 MPa ISO 527-1/-2
Strain at break 3.6 / 6.6 % ISO 527-1/-2
Flexural Modulus 7600 / - MPa ISO 178
Flexural Strength 214 / - MPa ISO 178
Charpy impact strength 　 　 ISO 179/1eU
23°C 97 / 96 kJ/m² 　
-40°C 109 / 97 kJ/m² 　
Charpy notched impact strength 　 　 ISO 179/1eA
23°C 20 / 27 kJ/m² 　
-30°C 18 / 17 kJ/m² 　
-40°C 18 / - kJ/m² 　
Izod notched impact strength 　 　 ISO 180/1A
23°C 21/26 kJ/m² 　
-30°C 17/16 kJ/m² 　
-40°C 15/- kJ/m² 　
Izod impact strength, -30°C 87/- kJ/m² ISO 180/1U
Thermal properties dry/cond Unit Test Standard
Melting temperature, 10°C/min 262/* °C ISO 11357-1/-3
Temp. of deflection under load 　 　 ISO 75-1/-2
1.8 MPa 245/* °C 　
0.45 MPa 261/* °C 　
Coeff. of linear therm. expansion, parallel 15/* E-6/K ISO 11359-1/-2
Coeff. of linear therm. expansion, normal 119/* E-6/K ISO 11359-1/-2
RTI, electrical, 0.75 mm 130/* °C UL 746B
RTI, impact 　 　 UL 746B
0.75 mm 65 °C 　
1.5mm 105 / * °C 　
RTI, strength 　 　 UL 746B
0.75 mm 85 °C 　
1.5mm 95 / * °C 　
3mm 105 °C 　
Flammability dry / cond Unit Test Standard
Burning Behav. at thickness h HB / * class IEC 60695-11-10
Thickness tested 0.75 / * mm IEC 60695-11-10
Electrical properties dry / cond Unit Test Standard
Comparative tracking index 400 / - - IEC 60112
Other properties dry / cond Unit Test Standard
Density 1330 / - kg/m³ ISO 1183
Water Absorption, Immersion 24h 0.91 / * % ASTM D 570
VDA Properties Value Unit Test Standard
Emission of organic compounds 25.3　µgC/g VDA 277
Odour 3　class VDA 270