PC 101沙伯基礎創新LEXAN Resin非鹵化壁厚部件用聚碳酸酯(13422875056)
Nonhalogenated, 7.0 MFR, for thicker sections without sinks.
Property
TYPICAL PROPERTIES (1)
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 630 kgf/cm² ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 700 kgf/cm² ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 7 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 135 % ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 990 kgf/cm² ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 23900 kgf/cm² ASTM D 790
Hardness, Rockwell M 70 - ASTM D 785
Hardness, Rockwell R 118 - ASTM D 785
Taber Abrasion, CS-17, 1 kg 10 mg/1000cy ASTM D 1044
IMPACT Value Unit Standard
Izod Impact, unnotched, 23°C 326 cm-kgf/cm ASTM D 4812
Izod Impact, notched, 23°C 92 cm-kgf/cm ASTM D 256
Tensile Impact, Type S 642 cm-kgf/cm² ASTM D 1822 |