PA6 BKV 215 H3.0 000000德國朗盛Durethan 15%玻纖增強熱老化穩定尼龍6塑料（18024445500）

PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized



ISO Shortname: ISO 1874-PA 6/66-HI, GHR, 14-040, GF15

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 280 °C / MT 80 °C; 400 bar % acc. ISO 2577 0.3　
Molding shrinkage, transverse 150x105x3; 280 °C / MT 80 °C; 400 bar % acc. ISO 2577 0.83　
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.05　
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.15　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 4500 2300
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 85 50
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 4.5 15
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 70 95
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 80 80
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 20 35
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 10 12
Izod impact strength 23 °C kJ/m² ISO 180-1U 60 90
Izod impact strength -30 °C kJ/m² ISO 180-1U 65 60
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 20 35
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 10 10
Flexural modulus 2 mm/min MPa ISO 178-A 4200 2300
Flexural strength 2 mm/min MPa ISO 178-A 135 75
Flexural strain at flexural strength 2 mm/min % ISO 178-A 5.5 8.5
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 125 55