PA6 BKV 30 FN00 000000德國朗盛Durethan 30%玻纖增強(qiáng)無鹵阻燃尼龍6塑料（18024445500）

PA 6, 30 % glass fibers, injection molding, halogen free flame retardant



ISO Shortname: ISO 1874-PA 6, GFHR, 14-110, GF30; ISO 1043-PA GF FR (30+40+72)

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Melt volume-flow rate 260 °C; 2.16 kg cm³/(10 min) ISO 1133-1 23　
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.22　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.62　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.08　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.18　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 10800 6700
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 150 90
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 6.1
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 60 65
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA <10　
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA <10　
Izod impact strength 23 °C kJ/m² ISO 180-1U 55 55
Izod notched impact strength 23 °C kJ/m² ISO 180-1A <10　
Izod notched impact strength -30 °C kJ/m² ISO 180-1A <10　
Flexural modulus 2 mm/min MPa ISO 178-A 9800 6000
Flexural strength 2 mm/min MPa ISO 178-A 210 140
Flexural strain at flexural strength 2 mm/min % ISO 178-A 2.7 4.6
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A　128

Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 224　
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 204　
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 218　
Vicat softening temperature 50 N; 120 °C/h °C ISO 306 210　
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.22　
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 0.81　
C Burning behavior UL 94 (1.6 mm)　Class UL 94 V-0　
Burning behavior UL 94 0.75 mm Class UL 94 V-0　
C Burning behavior UL 94-5V 1.6 mm Class UL 94 5VA　
C Oxygen index Method A % ISO 4589-2 32.1　
Glow wire test (GWFI) 0.8 mm °C IEC 60695-2-12 960　
Glow wire test (GWFI) 1.5 mm °C IEC 60695-2-12 960　
Glow wire test (GWFI) 3.0 mm °C IEC 60695-2-12 960　
Glow wire test (GWIT) 0.8 mm °C IEC 60695-2-13 775　
Glow wire test (GWIT) 1.5 mm °C IEC 60695-2-13 775　
Glow wire test (GWIT) 3.0 mm °C IEC 60695-2-13 800　

Electrical properties (23 °C/50 % r. h.)
C Electric strength 1 mm kV/mm IEC 60243-1 36.7　
C Comparative tracking index CTI Solution A V IEC 60112 600　

Other properties (23 °C)
C Water absorption (Saturation value) Water at 23 °C % ISO 62 5　
C Water absorption (Equilibrium value) 23 °C; 50 % RH % ISO 62 1.5　
C Density　kg/m³ ISO 1183 1427　

Processing conditions for test specimens
C Injection molding-Melt temperature　°C ISO 294 260　
C Injection molding-Mold temperature　°C ISO 294 80　

Processing recommendations
Drying temperature dry air dryer　°C - 80　
Drying time dry air dryer　h - 2-6　
Residual moisture content　% Acc. to Karl Fischer　0.03-0.07　
Melt temperature (Tmin - Tmax)　°C - 250-270　
Mold temperature　°C - 80-100　

C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.