PA6 B 30 S FN40 000000德國朗盛Durethan無鹵阻燃聚酰胺6尼龍塑料（18024445500）

PA 6, non-reinforced, injection molding, halogen free flame retardant



ISO Shortname: ISO 1874-PA 6, GFR, 14-030; ISO 1043-PA FR (30)　

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 260 °C / MT 80 °C; 500 bar % acc. ISO 2577 0.9　
Molding shrinkage, transverse 150x105x3; 260 °C / MT 80 °C; 500 bar % acc. ISO 2577 0.9　
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.2　
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.2　
C Molding shrinkage, parallel 60x60x2; 260 °C / MT 80 °C; 600 bar % ISO 294-4 0.9　
C Molding shrinkage, transverse 60x60x2; 260 °C / MT 80 °C; 600 bar % ISO 294-4 0.9　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.3　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.3　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 3400 1100
C Yield stress 50 mm/min MPa ISO 527-1,-2 90 45
C Yield strain 50 mm/min % ISO 527-1,-2 4.0 22.5
C Nominal strain at break 50 mm/min % ISO 527-1,-2 9.6 265
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 60 65
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 15.5 293
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU N N
Izod impact strength 23 °C kJ/m² ISO 180-1U N N
Izod notched impact strength 23 °C kJ/m² ISO 180-1A < 10　
Izod notched impact strength -30 °C kJ/m² ISO 180-1A < 10　
Flexural modulus 2 mm/min MPa ISO 178-A 3000 900