PA6 B 30 S F30 000000德國朗盛Durethan阻燃注塑成型聚酰胺6尼龍塑料(18024445500)
PA 6, non-reinforced, injection molding, flame retardant
ISO Shortname: ISO 1874-PA 6, GFHR, 14-040; ISO 1043-PA FR (17)
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 260 °C / MT 80 °C; 600 bar % ISO 294-4 1.1
C Molding shrinkage, transverse 60x60x2; 260 °C / MT 80 °C; 600 bar % ISO 294-4 1.1
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.4
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.4
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 3600
C Yield stress 50 mm/min MPa ISO 527-1,-2 70
C Yield strain 50 mm/min % ISO 527-1,-2 3,7
C Nominal strain at break 50 mm/min % ISO 527-1,-2 9.0
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 150
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 130
C Charpy notched impact strength 23 °C kJ/m&sup2; ISO 179-1eA <10
C Charpy notched impact strength -30 °C kJ/m&sup2; ISO 179-1eA <10
Izod impact strength 23 °C kJ/m&sup2; ISO 180-1U 120
Izod impact strength -30 °C kJ/m&sup2; ISO 180-1U 100 |