PA66 A 246M法國羅地亞TECHNYL®鞋底遙控汽車保險杠用尼龍66塑料（18024445500）

TECHNYL® A 246M 　 　 　 　
The values of properties are for natural grade. 　 　 　 　
Properties Standards Unit Values 　
　 　 　 d.a.m*. Cond.**
Physical 　 　 　 　
Water absorption (24 h at 23°C) ISO 62 % 1.05　-
Density ISO 1183-A g/cm3 1.08　-
Molding shrinkage Parallel (1) (RHODIA-EP) RHODIA-EP % 1.90　-
Molding shrinkage normal or perpendicular (1) (Rhodia EP) RHODIA-EP % 1.90　-
Molding Shrinkage Isotropy (Rhodia EP) RHODIA-EP 　 1　-
Mechanical 　 　 　 　
Tensile modulus ISO 527 type 1 A MPa 1900　600　
Tensile strength at yield ISO 527 type 1 A MPa 47　42　
Elongation at yield ISO 527 type 1 A % 20　210　
Tensile strength at break ISO 527 type 1 A MPa 44　35　
Flexural modulus ISO 178 MPa 1800　700　
Flexural maximum stress ISO 178 MPa 70　27　
Charpy notched impact strength ISO 179/1eA kJ/m2 97　100　
Charpy unnotched impact strength ISO 179/1eU kJ/m2 NB NB
Charpy unnotched impact strength (-30°C) ISO 179/1fU kJ/m2 16　-
Izod notched impact strength ISO 180/1A kJ/m2 60　80　
Izod notched impact strength (-30°C) ISO 180/1A kJ/m2 22　-
Flamability 　 　 　 　
Flammability UL 94 (Thickness 1,6 mm) ISO 1210/UL 94 　 HB -
Limit Oxygen index ISO 4589 　 24.5　-
Thermal 　 　 　 　
Melting Temperature ISO 11357 °C 263　-
Heat deflection temperature, 1,8 Mpa ISO 75/Af °C 65　-
Coef. of Linear thermal expansion parallel (23°C to 85°C) ISO 11359 E-5 / °C 7　-
Electrical 　 　 　 　
Relative permittivity IEC60250 　 3.20　4　
Dissipation factor IEC60250 　 0.02　0.06　
Volume resistivity IEC60093 Ohm.cm 10E14 10E12
Surface resistivity IEC60093 Ohm 10E13 10E12
Dielectric strength IEC60243 kV/mm 30　38　
Comparative tracking index sol. A IEC60112 Volt 575　600　
Comparative tracking index sol. B IEC60112 Volt 450　-